I-Polyvinylidene fluoride (PVDF)
Incazelo Yomkhiqizo
Ulwazi Oluyisisekelo.
| Ipharamitha | |
| Usayizi wezinhlayiya (D50) | ≤ 100mm |
| Ubuningi obuhlobene | 1.75-1.77 g/cm3 |
| Okuqukethwe komswakama | ≤ 0.15wt% |
| I-viscosity ejikelezayo, (7wt%, 25 ℃) | 1900-2900 mPa.s |
| Indawo yokuncibilika | 160-165 ℃ |
| Izinga lokushisa lokubola kokushisa | >360 ℃ |
| Isisindo esimaphakathi sesisindo sama-molecule | 80000-1200000 |
| Ukusatshalaliswa kwesisindo sama-molecule | 2.0~4.0“ |
| Ipharamitha | |
| Usayizi wezinhlayiya (D50) | ≤ 100mm |
| Ubuningi obuhlobene | 1.75-1.77 g/cm3 |
| Okuqukethwe komswakama | ≤ 0.10wt% |
| I-viscosity ejikelezayo, (7wt%, 25 ℃) | 2000-4000 mPa.s |
| Indawo yokuncibilika | 166-172 ℃ |
| Izinga lokushisa lokubola kokushisa | >360 ℃ |
| Isisindo esimaphakathi sesisindo sama-molecule | 80000-1200000 |
| Ukusatshalaliswa kwesisindo sama-molecule | 2.0~4.0“ |
| Ipharamitha | |
| Usayizi wezinhlayiya (D50) | ≤ 100mm |
| Ubuningi obuhlobene | 1.75-1.77 g/cm3 |
| Okuqukethwe komswakama | ≤ 0.10wt% |
| I-viscosity ejikelezayo, (7wt%, 25 ℃) | 5500-9500 mPa.s |
| Indawo yokuncibilika | 160-165 ℃ |
| Izinga lokushisa lokubola kokushisa | >360 ℃ |
| Isisindo esimaphakathi sesisindo sama-molecule | 1100000-1300000 |
| Ukusatshalaliswa kwesisindo sama-molecule | 2.0~4.0“ |
| Ipharamitha | |
| Usayizi wezinhlayiya (D50) |
|
| Ubuningi obuhlobene | 1.75-1.77g/cm³ |
| Okuqukethwe komswakama | ≤ 0.10wt% |
| I-viscosity ejikelezayo, (7wt%, 25 ℃) | 1500-4000mPa.s |
| Indawo yokuncibilika | 160-165 ℃ |
| Izinga lokushisa lokubola kokushisa | >375 ℃ |
| Isisindo esimaphakathi sesisindo sama-molecule | ≥ 580000 |
| Ukusatshalaliswa kwesisindo sama-molecule | 2.0-4.0“ |