Polyvinylidene fluoride (PVDF)
Product Description
Basic Info.
|
Parameter |
|
|
Particle size (D50) |
≤ 100mm |
|
Relative density |
1.75-1.77 g/cm3 |
|
Moisture content |
≤ 0.15wt% |
|
Rotational viscosity, (7wt%, 25 ℃) |
1900-2900 mPa. s |
|
Melting point |
160-165 ℃ |
|
Thermal decomposition temperature |
>360 ℃ |
|
Weight average molecular weight |
80000-1200000 |
|
Molecular weight distribution |
2.0~4.0“ |
|
Parameter |
|
|
Particle size (D50) |
≤ 100mm |
|
Relative density |
1.75-1.77 g/cm3 |
|
Moisture content |
≤ 0.10wt% |
|
Rotational viscosity, (7wt%, 25 ℃) |
2000-4000 mPa. s |
|
Melting point |
166-172 ℃ |
|
Thermal decomposition temperature |
>360 ℃ |
|
Weight average molecular weight |
80000-1200000 |
|
Molecular weight distribution |
2.0~4.0“ |
|
Parameter |
|
|
Particle size (D50) |
≤ 100mm |
|
Relative density |
1.75-1.77 g/cm3 |
|
Moisture content |
≤ 0.10wt% |
|
Rotational viscosity, (7wt%, 25 ℃) |
5500-9500 mPa. s |
|
Melting point |
160-165 ℃ |
|
Thermal decomposition temperature |
>360 ℃ |
|
Weight average molecular weight |
1100000-1300000 |
|
Molecular weight distribution |
2.0~4.0“ |
|
Parameter |
|
|
Particle size (D50) |
<35mm |
|
Relative density |
1.75-1.77g/cm ³ |
|
Moisture content |
≤ 0.10wt% |
|
Rotational viscosity, (7wt%, 25 ℃) |
1500-4000mPa. s |
|
Melting point |
160-165 ℃ |
|
Thermal decomposition temperature |
>375 ℃ |
|
Weight average molecular weight |
≥ 580000 |
|
Molecular weight distribution |
2.0-4.0“ |