Polivinilidena fluorida (PVDF)
Katrangan Produk
Informasi Dhasar.
| Parameter | |
| Ukuran partikel (D50) | ≤ 100mm |
| Kapadhetan relatif | 1,75-1,77 g/cm3 |
| Kadar banyu | ≤ 0.15wt% |
| Viskositas rotasi, (7wt%, 25 ℃) | 1900-2900 mPa. s |
| Titik leleh | 160-165 ℃ |
| Suhu dekomposisi termal | >360 ℃ |
| Bobot rata-rata bobot molekul | 80000-1200000 |
| Distribusi bobot molekul | 2.0~4.0“ |
| Parameter | |
| Ukuran partikel (D50) | ≤ 100mm |
| Kapadhetan relatif | 1,75-1,77 g/cm3 |
| Kadar banyu | ≤ 0.10wt% |
| Viskositas rotasi, (7wt%, 25 ℃) | 2000-4000 mPa. s |
| Titik leleh | 166-172 ℃ |
| Suhu dekomposisi termal | >360 ℃ |
| Bobot rata-rata bobot molekul | 80000-1200000 |
| Distribusi bobot molekul | 2.0~4.0“ |
| Parameter | |
| Ukuran partikel (D50) | ≤ 100mm |
| Kapadhetan relatif | 1,75-1,77 g/cm3 |
| Kadar banyu | ≤ 0.10wt% |
| Viskositas rotasi, (7wt%, 25 ℃) | 5500-9500 mPa. s |
| Titik leleh | 160-165 ℃ |
| Suhu dekomposisi termal | >360 ℃ |
| Bobot rata-rata bobot molekul | 1100000-1300000 |
| Distribusi bobot molekul | 2.0~4.0“ |
| Parameter | |
| Ukuran partikel (D50) |
|
| Kapadhetan relatif | 1,75-1,77g/cm³ |
| Kadar banyu | ≤ 0.10wt% |
| Viskositas rotasi, (7wt%, 25 ℃) | 1500-4000mPa. s |
| Titik leleh | 160-165 ℃ |
| Suhu dekomposisi termal | >375 ℃ |
| Bobot rata-rata bobot molekul | ≥ 580000 |
| Distribusi bobot molekul | 2.0-4.0“ |